文獻名：Acid hydrolysis of kraft lignin-acrylamide polymer to improve its flocculation affinity
作者： Malak Aldajania, Niloofar Alipoormazandarania, Fangong Kongb, Pedram Fatehiab
a Department of Chemical Engineering, Lakehead University, 955 Oliver Road, Thunder Bay, Ontario P7B 5E1, Canada
b State Key Laboratory of Biobased Material and Green Papermaking, Qilu University of Technology (Shandong Academy of Sciences), Jinan, Shandong 250353, China
摘要：To explore the production of anionic lignin polymer with a high charge density as a flocculant, lignin-acrylamide (KL-AM) was generated and subsequently hydrolyzed under various conditions. The hydrolysis reaction was optimized to generate the anionic lignin polymer with high anionicity. KL-AM and hydrolyzed lignin polymer (HKL-AM) had a molecular weight of 1564 kg/mol and 601 kg/mol and charge density of −2.33 meq/g and −3.62 meq/g, respectively. Adsorption, turbidity, mass balance, and chord length analyses confirmed the more efficient flocculation affinity of HKL-AM than KL-AM and polyAM in flocculating aluminum oxide particles in suspension systems. The results also indicated that the charge density of the lignin derivative was contributed greatly to the strength of flocs, but the molecular weight of the macromolecule significantly affected the deflocculation tendency of the particles. The results confirmed that the hydrolysis could be used as a reliable approach to improve the anionicity of lignin-acrylamide polymers and thus the flocculation affinity of the polymers at the expense of a molecular weight drop.
關(guān)鍵詞：Kraft lignin; Acrylamide; Flocculant; Aluminum oxide suspension
|